| FABRIC SPECIFICATIONS |
| Construction |
Reinforcing polyester scrim between polypropylene barrier layers |
| Colour |
Black, and other colors available after construction |
| Weight |
16 oz/yd2 (542 g/m2) +/- 5% |
| Thickness |
Nominal 24 mils -0.024" (0.61mm) |
| PERFORMANCE |
| Grab Tensile |
Warp 274 lb 1218 N |
Weft 230 lb 1026 N |
ASTM D751/NSF |
| Tongue Tear |
Warp 73 lb 324 N |
Weft 48 lb 213 N |
ASTM D2261-96 |
| Tongue Tear - Large Scale |
Warp 141 lb 628 N |
Weft 168 lb 746 N |
ASTM D5884-01 |
| Trapezoidal Tear |
Warp 138 lb 613 N |
Weft 75 lb 333 N |
ASTM D4533-04 |
| Mullen Burst |
338 psi 2332 kPa |
|
ASTM D3786-01 |
| Hydrostatic Resistance |
328 psi 2265 kPa |
|
ASTM D751-00 |
| Puncture Resistance |
89 lb 395 N |
|
ASTM D4833-00 |
| Puncture Resistance |
352 lb 1565 N |
|
FTMS 101C, 2031 |
| Carbon Black Content |
4.57% |
|
ASTM D4218-96 |
| Carbon Black Dispersion |
Rating = 1 |
|
ASTM D5596-03 |
| Volatile Loss |
0.23% |
|
ASTM D1203-94 |
| Dimensional Stability |
Warp -0.33% |
Weft 0.03% |
ASTM D1204-02 |
| Low Temperature Flex |
Warp Pass @ -40% |
Weft Pass @ -40% |
ASTM D2136-94 |
| Accelerated UV Weathering1 |
100% strength retention after 2000 hrs
exposure @ 0.77 W/m2/nm, or 1200 hours
exposure @ 1.35 W/m2/nm. |
ASTM G151-00
ASTM G154-04 |
 |
| 1 Q.U.V. [A-340 Lamps}: 8 hrs UV @ 60˚ C; 4 hrs condensation @ 50˚ C |
|
These values are typical data and are not intended as limiting specifications.
NOTE: All cut edges where the scrim is exposed must be sealed using Nova-Thene AquaMaster™ PP welding rod. |
|
| WARRANTY |
| A 15 year limited warranty is offered on liner applications. Contact your IPG representative for further details. |
| |
|