| FABRIC SPECIFICATIONS |
| Construction |
Reinforcing polyester scrim between LLDPE barrier layers |
| Colour |
Black, and other colors available after consultation |
| Weight |
16 oz/yd2 (542 g/m2) +/- 5% |
| Thickness |
Nominal 24 mils ( 0.61 mm) |
| PERFORMANCE |
| Grab Tensile |
Warp 258 lb 1150 N |
Weft 250 lb 1114 N |
ASTM D751/NSF |
| Tongue Tear |
Warp 120 lb 532 N |
Weft 160 lb 710 N |
ASTM D2261-96 |
| Tongue Tear - Large Scale |
Warp 140 lb 621 N |
Weft 149 lb 663 N |
ASTM D5884-01 |
| Trapezoidal Tear |
Warp 200 lb 890 N |
Weft 130 lb 578 N |
ASTM D4533-04 |
| Mullen Burst |
370 psi 2553 kPa |
|
ASTM D3786-01 |
| HYDROSTATIC RESISTANCE |
208 psi 1438 kPa |
|
ASTM D751-00 |
| PUNCTURE RESISTANCE |
76 lb 339 N |
|
ASTM D4833-00 |
| CARBON BLACK CONTENT |
3.71 % |
|
ASTM D4218-96 |
| CARBON BLACK DISPERSION |
Rating = 1 |
|
ASTM D5596-03 |
| VOLATILE LOSS |
0.07 % |
|
ASTM D1203-94 |
| DIMENSIONAL STABILITY |
Warp -1.40 % |
Weft -1.34 % |
ASTM D1204-02 |
| LOW TEMPERATURE FLEX |
Warp Pass @ -40° |
Weft Pass @ -40° |
ASTM D2136-94 |
| Accelerated UV Weathering1 |
>95% strength retention after 2000 hrs exposure @
0.77 W/m2/nm, or 1200 hours exposure @ 1.35
W/m2/nm. |
ASTM G151-00
ASTM G154-04 |
 |
| 1 Q.U.V. [A-340 Lamps}: 8 hrs UV @ 60˚ C; 4 hrs condensation @ 50˚ C |
|
| These values are typical data and are not intended as limiting specifications. |
|
| NOTE: All cut edges where the scrim is exposed must be sealed using AquaMaster PE welding rod. |
|
| WARRANTY:
A 15 year limited warranty is offered on liner applications. Contact your IPG representative for further details. |
|